3D Pro Multilayer

The ICERA 3D Pro Multilayer is a high-performance multilayer dental zirconia block engineered as the ultimate all-purpose solution for modern dental laboratories. Combining advanced three-dimensional gradient technology, premium raw materials, and refined manufacturing, the 3D Pro Multilayer delivers natural shade transitions, exceptional translucency (up to 49%), and high cervical strength (up to 1200 MPa). Whether the case calls for a single anterior crown, a long-span posterior bridge, or a full-arch reconstruction, the 3D Pro Multilayer is engineered to perform.

The 3D Pro Multilayer features a sophisticated multilayer color gradient with a dominant main color occupying 60% of the disc — minimizing color discrepancy on teeth with strong curvatures and ensuring predictable shade reproduction across complex restorations. Translucency transitions naturally from 42% at the cervical to 49% at the incisal, replicating the optical depth of natural enamel. Simultaneously, flexural strength gradients from 700 MPa at the incisal to 1200 MPa at the cervical, providing reliable structural support exactly where it's needed most. This dual-gradient design makes the 3D Pro Multilayer one of the most clinically versatile zirconia options available today.

・Product Name: ICERA 3D Pro Multilayer
・Category: Multilayer Dental Zirconia Block
・Translucency: 42%–49% (graded across layers)
・Flexural Strength: 700–1200 MPa (graded across layers)
・Disc Diameter: 98mm (standard), custom sizes available
・Disc Thickness: 10mm / 12mm / 14mm / 16mm / 18mm / 20mm / 22mm / 25mm
・Shade System: VITA 16 classical shades plus bleach shades
・Compatibility: All open-system CAD/CAM milling machines
・Standards: ISO 13356, FDA certified, biocompatible

1. Optimized 60% Main-Color Distribution Unlike conventional multilayer zirconia where color layers are distributed evenly, the 3D Pro Multilayer concentrates 60% of the disc in the main color zone. This produces dramatically reduced color discrepancies on teeth with strong curvatures — a key advantage for premolars, canines, and contoured anterior cases.
2. Wide Translucency Range (42%–49%) With translucency reaching up to 49% at the incisal edge, the 3D Pro Multilayer achieves enamel-like optical realism. Meanwhile, the cervical's 42% translucency provides essential masking over discolored abutments — a balance rarely achieved in a single disc.
3. High Strength (700–1200 MPa) With cervical strength reaching 1200 MPa, the 3D Pro Multilayer is rated for full-arch and long-span bridge restorations, while the lower incisal strength provides gentle, enamel-friendly occlusal contact.
4. Universal 1530°C Sintering Compatibility The 1530°C sintering temperature works seamlessly with virtually all major sintering furnace brands and protocols. The 3D Pro Multilayer is highly tolerant to minor temperature fluctuations, ensuring consistent results regardless of equipment.
5. Rapid Sintering for 1–6 Unit Restorations A specially optimized fast-sintering curve completes 6-unit bridges in just 2 hours and 50 minutes — significantly accelerating production while maintaining full mechanical and aesthetic properties.
6. Minimal Inter-Layer Shrinkage Variation Layer-to-layer shrinkage variation is only 0.16%, meaning frameworks remain dimensionally accurate after sintering — minimizing distortion on long-span cases.
7. Outstanding Sintered Density (≥6.0 g/cm³) A dense, pore-free post-sintering microstructure ensures fracture resistance, color stability, and long-term clinical durability.
8. Excellent Biocompatibility & Safety With Grade 0 cytotoxicity, radioactivity below 0.1 Bq/g, and chemical solubility below 100 μg/cm², the 3D Pro Multilayer is fully safe for permanent intraoral use.

The ICERA 3D Pro Multilayer is engineered for the broadest possible range of indications:
・Veneers – with up to 49% incisal translucency
・Inlays and onlays
・Anterior single crowns
・Posterior single crowns
・Full-contour crowns
・Multi-unit bridges – including long-span and full-arch
・Implant-supported crowns and bridges
・Cosmetic smile design cases
・6-unit bridges – with rapid sintering support

The 3D Pro Multilayer represents ICERA's commitment to combining material science with practical lab needs. Manufactured using Sinocera raw zirconia powders, every disc undergoes high-pressure cold isostatic pressing (CIP), precision pre-sintering, and proprietary multi-layer color infiltration — followed by strict batch-by-batch quality inspection covering flexural strength, translucency, density, and shade accuracy.

For dental laboratories seeking a single zirconia material that performs across the entire clinical spectrum — anterior beauty, posterior strength, and everything in between — the ICERA 3D Pro Multilayer is the smart, cost-effective choice. It simplifies your workflow, reduces material costs, and delivers consistently outstanding restorations that satisfy clinicians and patients alike.

Choose ICERA 3D Pro Multilayer — the universal multilayer zirconia disc engineered for modern digital dentistry.